軋鋼生產的工序十分復雜，盡管隨著軋制質量要求的提高，品種范圍的擴大以及新技術，新設備的應用，組成工藝過程的各個工序都會有相應的變化.

The process of rolling production is very complicated. Although all the processes of the process will be changed along with the improvement of rolling quality requirements, the expansion of varieties and the application of new technology and new equipment.

棒材穿水冷卻裝置的基本原理是什么？

在精軋機后設有一個由數個水冷箱組成的可調水冷段，對棒材進行急劇冷卻，使棒材表面形成馬氏體組織，在隨后的溫度恢復過程中，芯部熱量散出對表面馬氏體組織可產生回火作用，結果棒材表面層為回火馬氏體，芯部為細粒珠光體及索氏體組織。這種組織結構使棒材屈服極限和韌性提高，并具有良好的可焊性。Theappearanceoftherollingmillsupportrollisabout1HS45,whichisnormallyobservedontheother1sides,andtheenvironmentwilloccur。

What is the basic principle of the bar water cooling device?

After the finishing mill, there is an adjustable water cooling section  of several water cooling boxes. The rod material is cooled sharply to form martensite structure. During the subsequent temperature recovery process, the heat of the core can produce tempering on the surface martensite, and the surface layer of the rod is tempered martensite, the core is fine pearlite and Soxhlet body. This structure improves the yield limit and toughness of bars, and has good solderability.

采用控制軋制工藝時，為了防止原始奧氏體晶粒過分長大，一般采用較低的加熱溫度和開軋溫度。由于開軋溫度高，變形后的奧氏體晶粒會發生再結晶而細化，如在這個階段停止變第八節控制軋制技術形，軋件即隨溫度下降而產生相變。

In order to prevent the original austenite grain growing too much, the lower heating temperature and rolling temperature are generally adopted in the rolling process. Due to the high rolling temperature, the austenite grain after the deformation will be recrystallized and refined. For example, the eighth section  rolling technology is stopped at this stage, and the phase change is produced as the temperature drops.